Applications of Insole Foot Care Making clear Silicone
Applied directly to human skin.
Used for making prosthetic appliances,
cushioning for orthotics devices
special effect orthotic devices,
skin safe appliances and effects, etc.
Some are certified “food safe” for culinary applications
Features of Insole Foot Care Making clear Silicone
Soft and Stretchy
Soft, Softer, Softest
Operation of Insole Foot Care Making clear Silicone
1.Put silicone part A and part B(platinum silicone is made of part A and part B, the mixed ratio is 1:1 ) into two pipe(the machine has two pipes)
2.When they mix together in one pipe, liquid silicone will be injected into the Aluminum molds
3.when they are into the Aluminum molds, liquid silicone will be cured after several minutes(the temperature of the Aluminum mold is from 60℃ to 150℃)
4. take of the cured silicone(silicone product) from the molds.
Package of Insole Foot Care Making clear Silicone
1kg/can, 5kg/can, 20kg/drum, 200kg/drum
Insole Foot Care Making clear Silicone Packaging & Shipping:
Sample packaging: 1kg
Cargo packaging: metal drum and plastic drum:5kg 20kg, 25kg and 200kg
Shippping: Transport as non-dangerous Article
Product Name: Insole Foot Care Making clear Silicone
Product Style.: ZHUOERWEI E
Brand: ZEW silicone
Insole Foot Care Making clear Silicone usage:
Applied directly to human skin.
Used for making prosthetic appliances, cushioning for orthotics devices and special effect orthotic devices, skin safe appliances and effects, etc. Some are certified “food safe” for culinary applications
Notes: The data are based on the operation under room temperature of 25℃
Typical general characteristics |
Inspection Method |
ZEWS05 |
ZEWS10 |
ZEWS15 |
ZEWS30 |
Product data (Catalyzed A+B) | |||||
Hardness | Shore A | 5±2 | 10±2 | 15±2 | 30±2 |
Mix Ratio | A:B | 1:1 | 1:1 | 1:1 | 1:1 |
Color | / | Clear | Clear | Clear | Clear |
Pot life | 25 °C (77F) | 10-20mins | 10-20mins | 10-20mins | 10-20mins |
Curing time | 25 °C (77F) | 4- 6hrs | 4- 6hrs | 4- 6hrs | 4- 6hrs |
Viscosity | mPa.s | 3000±2000 | 4000±2000 | 8000±2000 | 15000±2000 |
Tear-Strength | kg/cm | ≥13 | ≥15 | ≥18 | ≥25 |
Tensile -Strength | M.pa | ≥2.8 | ≥3.8 | ≥4.2 | ≥4.1 |
Elongation | % | ≥500 | ≥500 | ≥420 | ≥380 |
Shrinkage | % | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 |